    Posted: November 22 2006 at 7:59am
Are any of the marine apoxy's safe to use ? I bought a tube of lock tight marine apoxy at lowes but have not used it yet. From the package it seemed like it was ideal stating that it would cure underwater.
I have never used apoxy for frags before. I just wanted something a bit stronger than super glue for large pieces
Contact me for professional aquarium maintenance and localy grown coral frags. [URL=http://www.aquatitranquility.com][/URL]

Back to Top
Lyscer View Drop Down
Guest
Guest
Avatar

Joined: May 20 2005
Location: Layton
Status: Offline
Points: 1565
Post Options Post Options   Thanks (0) Thanks(0)   Quote Lyscer Quote  Post ReplyReply Direct Link To This Post Posted: November 22 2006 at 8:52am
Bruce I use aquamend from home depot. It is the two-part epoxy. I used it to epoxy my rocks together and haven't had any problems at all. I do run a skimmer 24/7 though. I would say if it is two part and since you bought it, just use a little and monitor everything closely. If things look even a little wierd I would do a small water change and pull it out.
Back to Top
Mike Savage View Drop Down
Guest
Guest
Avatar

Joined: July 15 2005
Location: Murray
Status: Offline
Points: 19173
Post Options Post Options   Thanks (0) Thanks(0)   Quote Mike Savage Quote  Post ReplyReply Direct Link To This Post Posted: November 24 2006 at 5:01pm
I too use Aquamend from HD.


Back to Top
 Post Reply Post Reply
  Share Topic   

Forum Jump Forum Permissions View Drop Down

Forum Software by Web Wiz Forums® version 12.03
Copyright ©2001-2018 Web Wiz Ltd.

This page was generated in 0.109 seconds.